Core Selection Data
Reference Values for Early Screening
| Property | Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm3 | ISO 1183 |
| Melt Flow Rate (MFI) | 4 | g/10 min | ISO 1133, 195 °C/2.16 kg |
| Molding Shrinkage | 0.7-1.0 | % | Internal Method |
| Tensile Strength | 113 | MPa | ISO 527 |
| Tensile Modulus | 7000 | MPa | ISO 527 |
| Flexural Modulus | 6200 | MPa | ISO 178 |
| Charpy Notched Impact Strength | 6.8 | kJ/m2 | ISO 179/1eA |
| Heat Deflection Temperature | 163 | °C | ISO 75-2, 1.8 MPa |
Suggested maximum moisture for POM processing: 0.2-0.4 %
Core comparison values are shown here. Full property, processing, impact, electrical, and project-specific data are provided through TDS or project review.
Request Full TDSKey Features
- 20% Glass Fiber Content
- High Stiffness
- Lower Molding Shrinkage
Typical Applications
- Automotive Functional Parts
- Precision Components
- Structural Molded Parts
Material Evaluation Notes
This product page is for preliminary material selection. For project evaluation, please confirm the application, processing method, mold development stage, cavity count, target shrinkage or dimensional requirement, target performance requirements, current reference grade, document requirements, and estimated volume.