Core Selection Data
Reference Values for Early Screening
| Property | Value | Unit | Test Method |
|---|---|---|---|
| Specific gravity | 1.21 | ISO 1183 | |
| Tensile stress | 110 | MPa | ISO 527 |
| Tensile modulus | 5100 | MPa | ISO 527 |
| Flexural modulus | 4950 | MPa | ISO 178 |
| Charpy impact strength(Notched) @ 23 °C | 9.5 | kJ/m2 | ISO 179/1eA |
| Heat deflection temperature (1.8 MPa) | 195 | °C | ISO 75 |
Core comparison values are shown here. Full property, processing, impact, electrical, and project-specific data are provided through TDS or project review.
Request Full TDSGrade Characteristics
- EAG115U publishes higher notched impact than EAG115 and EAG115H, while its tensile stress, flexural modulus, flexural strength and HDT are lower than the corresponding EAG115 values.
- 15% filler or reinforcement reference
- HB flammability reference
Typical Applications
- Clips
- protective housings
- brackets and molded components where the published notched-impact result is prioritized within the 15% glass-fiber PA6 group.
Material Evaluation Notes
Use the comparison only for initial screening under the listed test conditions. Confirm moisture-conditioned behavior, geometry sensitivity, joining loads and end-use impact requirements on the actual part.
Inquiry Preparation
Prepare a Grade Evaluation
Send the application, key performance requirements, mold stage, cavity count, dimensional concern, current material or reference grade, document needs, and estimated volume. These inputs identify the next grade, document, and sample steps for the project.