Core Selection Data
Reference Values for Early Screening
| Property | Value | Unit | Test Method |
|---|---|---|---|
| Specific gravity | 1.29 | ISO 1183 | |
| Tensile stress | 125 | MPa | ISO 527 |
| Flexural modulus | 6500 | MPa | ISO 178 |
| Charpy impact strength(Notched) @ 23 °C | 5.5 | kJ/m2 | ISO 179/1eA |
| Heat deflection temperature (1.8 MPa) | 205 | °C | ISO 75 |
Core comparison values are shown here. Full property, processing, impact, electrical, and project-specific data are provided through TDS or project review.
Request Full TDSGrade Characteristics
- Against EAG120U at the same listed glass-fiber content, EAG120 has a slightly higher published flexural modulus, while EAG120U publishes higher tensile stress, flexural strength, notched impact and HDT.
- 20% filler or reinforcement reference
- HB flammability reference
Typical Applications
- Structural housings
- brackets and molded supports evaluated around a 20% glass-fiber PA6 starting point and a 6500 MPa published flexural modulus.
Material Evaluation Notes
Compare both 20% grades using the same specimen conditioning and test methods, then confirm flow, fiber orientation, warpage and mechanical performance in the intended mold.
Inquiry Preparation
Prepare a Grade Evaluation
Send the application, key performance requirements, mold stage, cavity count, dimensional concern, current material or reference grade, document needs, and estimated volume. These inputs identify the next grade, document, and sample steps for the project.