| Property | Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.5 | g/cm3 | ISO 1183 |
| Melt Flow Rate (MFI) | 7.5 | g/10 min | ISO 1133, 195 °C/2.16 kg |
| Molding Shrinkage | 1.8-2.0 | % | Internal Method |
| Tensile Strength | 42 | MPa | ISO 527 |
| Flexural Modulus | 1650 | MPa | ISO 178 |
| Charpy Notched Impact Strength | 5 | kJ/m2 | ISO 179/1eA |
| Heat Deflection Temperature | 100 | °C | ISO 75-2, 1.8 MPa |
Suggested maximum moisture for POM processing: 0.2-0.4 %
Core comparison values are shown here. Full property, processing, impact, electrical, and project-specific data are provided through TDS or project review.
Request Full TDSKey Features
- PTFE-Filled Formulation
- Wear-Resistant POM
- For Sliding Components
Typical Applications
- Sliding Parts
- Bushings
- Gears
- Industrial Molded Parts
Material Evaluation Notes
Use these reference values for preliminary screening only. Confirm final suitability with current technical documents, molded-part trials, processing conditions, and project-specific requirements.
Continue the comparison with the PTFE and low-friction POM selection guide or the wear-resistant and low-friction POM grades or the low-friction POM solution options.
Inquiry Preparation
Prepare a Grade Evaluation
Send the application, key performance requirements, mold stage, cavity count, shrinkage or warpage concern, current material or reference grade, document needs, and estimated volume. These inputs identify the next grade, document, and sample steps for the project.